Mechanical properties of self-compacting concrete with recycled bead wires

Mehmet Alpaslan Köroglu, Ashraf Ashour

Abstract


DOI: 10.7764/RDLC.18.3.501

This paper investigates the properties of self-compacting concrete with waste steel bead wires obtained as a result of the separation of waste tires. Waste steel bead wires were added to concrete between 1% and 5% by weight with an increment of 1%. In total, 54 cubes, 6 cylinders and 6 beams were cast, cured and tested in according to various standards to obtain the compressive, splitting tensile and flexural strengths, respectively. In addition, 6 cubes were left in salty water solution with a salt concentration of 4% for 120 days and tested in compression. A scanning electron microscopy (SEM) was also conducted on samples after failure. Test results showed that short time corrosion of steel fibers does not affect the mechanical properties. Also, the increase in the ratio of steel fiber was found to contribute positively to the mechanical properties of concrete up to 4%, beyond which, mechanical properties were reduced. Finally, in the samples subjected to bending tests, it has been found that a 6-fold increase in bending strength compared to the reference (non-fiber) sample was achieved in case of steel fiber ratio of 4% and 5%.

 

 

 


Keywords


Recycling, waste steel fibers, Non-Destructive, electron scanning microscopy, self-compacting

Full Text:

PDF

Refbacks

  • There are currently no refbacks.