Influences of high temperature on mechanical properties of fly ash based geopolymer mortars reinforced with PVA fiber


  • Mehmet Kaya Department of Civil Engineering, Yozgat Bozok University Yozgat, 66900 (Turkey)
  • Fuat Köksal Department of Civil Engineering, Yozgat Bozok University Yozgat, 66900 (Turkey)



fly ash, polyvinyl alcohol, high temperature, flexural strength, compressive strength, geopolymer


In this study, a geopolymer composite containing PVA fiber was produced to recycle waste fly ash and obtain an eco-friendly binder. Mechanical properties of geopolymer mortars, produced by using F class fly ash which was activated with NaOH (sodium hydroxide), and reinforced by PVA (polyvinyl alcohol) fiber were investigated after high temperature effect. Geopolymer mortar samples produced by mixing with fly ash, sand, water and NaOH were placed in standard molds of 40×40×160 mm3. PVA fibers were used at percentages of 0,5%, 1% and 1,5% by volume in the experiment. Tests were performed on mortars exposed to high temperatures of 200°C, 400°C, 600°C and 800°C for physical and mechanical properties. For the specimens not subjected to high temperatures, an increase in the compressive strength of mortars containing PVA fibers was observed in comparison to mortar without PVA fiber. On the other hand, it was concluded that losses in compressive strength were less for mortar without PVA fiber when compared with the mortars containing PVA fibers. As a result of the modeling, the PVA ratio, which gives the optimum flexural and compressive strength, was determined as 1,47%. As a result of melting of PVA fibers under the effect of high temperature, 83,58% loss of compressive strength was determined in samples containing 1,5% PVA after 800ºC temperature.


Download data is not yet available.

Author Biography

Fuat Köksal, Department of Civil Engineering, Yozgat Bozok University Yozgat, 66900 (Turkey)

Department of Civil Engineering, Yozgat Bozok University

Yozgat, 66900 (Turkey)


Abdullah, Alida, Ku Amirrul Rahman Ku Yin, Mohd Mustafa Al Bakri Abdullah, Kamarudin Hussin, and Mien Van Tran. 2015. “Comparison of Mechanical Properties of Fly Ash Artificial Geopolymer Aggregates with Natural Aggregate.” Applied Mechanics and Materials (Vol. 754, pp. 290-295). Trans Tech Publications Ltd. doi: 10.4028/

Alomayri, Thamer. 2019. “Experimental Study of the Microstructural and Mechanical Properties of Geopolymer Paste with Nano Material (Al2O3).” Journal of Building Engineering 25, 100788. doi: 10.1016/j.jobe.2019.100788.

American Coal Ash Association. 2020.

Applications, Science, and Sustainability of Coal Ash. 2020.

Arısoy B. 2002. “Development and Fracture Evaluation of High Performance Fiber Reinforced Lightweight Concrete.” Wayne State University.

Atabey, İsmail İsa, Okan Karahan, Cahit Bilim, and Cengiz Duran Atiş. 2020. “The Influence of Activator Type and Quantity on the Transport Properties of Class F Fly Ash Geopolymer.” Construction and Building Materials 264. doi: 10.1016/j.conbuildmat.2020.120268.

Atiş, C. D., E. B. Görür, O. Karahan, C. Bilim, S. Ilkentapar, and E. Luga. 2015. “Very High Strength (120 MPa) Class F Fly Ash Geopolymer Mortar Activated at Different NaOH Amount, Heat Curing Temperature and Heat Curing Duration.” Construction and Building Materials 96, 673.678. doi: 10.1016/j.conbuildmat.2015.08.089.

Aydın S. 2010. “Development of a Fiber Reinforced Composite with Alkali Activated Ground Granulated Blast Furnace Slag.” The Graduate School of Natural and Applied Sciences.

Aygörmez, Yurdakul. 2021. “Performance of Ambient and Freezing-Thawing Cured Metazeolite and Slag Based Geopolymer Composites against Elevated Temperatures.” Revista de La Construcción 20(1). doi: 10.7764/RDLC.20.1.145.

Balcikanli, Müzeyyen, and Erdogan Ozbay. 2016. “Optimum Design of Alkali Activated Slag Concretes for the Low Oxygen/Chloride Ion Permeability and Thermal Conductivity.” Composites Part B: Engineering, 91, 243-256. doi: 10.1016/j.compositesb.2016.01.047.

Bernal, Susan A., Ruby Mejía de Gutierrez, John L. Provis, and Volker Rose. 2010. “Effect of Silicate Modulus and Metakaolin Incorporation on the Carbonation of Alkali Silicate-Activated Slags.” Cement and Concrete Research, 40(6), 898-907. doi: 10.1016/j.cemconres.2010.02.003.

Bingöl, Şinasi, Cahit Bilim, Cengiz Duran Atiş, Uğur Durak, Serhan İlkentapar, and Okan Karahan. 2020. “An Investigation of Resistance of Sodium Meta Silicate Activated Slag Mortar to Acidic and Basic Mediums.” Revista de La Construcción, 19(1), 127-133. doi: 10.7764/rdlc.19.1.127-133.

Çelikten, Serhat. 2021. “Mechanical and Microstructural Properties of Waste Andesite Dust-Based Geopolymer Mortars.” Advanced Powder Technology 32(1), 1–9. doi: 10.1016/j.apt.2020.10.011.

Çelikten, Serhat, Mustafa Sarıdemir, and İbrahim Özgür Deneme. 2019. “Mechanical and Microstructural Properties of Alkali-Activated Slag and Slag + fly Ash Mortars Exposed to High Temperature.” Construction and Building Materials, 217, 50–61. doi: 10.1016/j.conbuildmat.2019.05.055.

Chindaprasirt, Prinya, Siwanant Thaiwitcharoen, Supranee Kaewpirom, and Ubolluk Rattanasak. 2013. “Controlling Ettringite Formation in FBC Fly Ash Geopolymer Concrete.” Cement and Concrete Composites, 41, 24-28. doi: 10.1016/j.cemconcomp.2013.04.009.

Davidovits, J. 1989. “Geopolymers and Geopolymeric Materials.” Journal of Thermal Analysis 35(2), 429-441. doi: 10.1007/BF01904446.

DeMerlis, C. C., and D. R. Schoneker. 2003. “Review of the Oral Toxicity of Polyvinyl Alcohol (PVA).” Food and Chemical Toxicology, 41(3), 319-326.

Derringer, George, and Ronald Suich. 1980. “Simultaneous Optimization of Several Response Variables.” Journal of Quality Technology, 12(4), 214-219. doi: 10.1080/00224065.1980.11980968.

Diaz-Loya, E. Ivan, Erez N. Allouche, and Saiprasad Vaidya. 2011. “Mechanical Properties of Fly-Ash-Based Geopolymer Concrete.” ACI Materials Journal, 108(3), 300–306. doi: 10.14359/51682495.

Durak, Ugur, Serhan İlkentapar, Okan Karahan, Burak Uzal, and Cengiz Duran Atiş. 2021. “A New Parameter Influencing the Reaction Kinetics and Properties of Fly Ash Based Geopolymers: A Pre-Rest Period before Heat Curing.” Journal of Building Engineering 35, 102023. doi: 10.1016/j.jobe.2020.102023.

Durak, Uğur, Okan Karahan, Burak Uzal, Serhan İlkentapar, and Cengiz Duran Atiş. 2021. “Influence of Nano SiO2 and Nano CaCO3 Particles on Strength, Workability, and Microstructural Properties of Fly Ash‐based Geopolymer.” Structural Concrete 22(S1), E352-E367. doi: 10.1002/suco.201900479.

Elyamany, Hafez E., Abd Elmoaty M. Abd Elmoaty, and Ahmed M. Elshaboury. 2018. “Magnesium Sulfate Resistance of Geopolymer Mortar.” Construction and Building Materials, 184, 111-127. doi: 10.1016/j.conbuildmat.2018.06.212

Global Carbon Atlas. 2020. Retrieved (

Jones, J. I. 1973. Polyvinyl Alcohol. Properties and Applications. UK: Jhon Wiley, Chichester.

Kaur, Mandeep, Jaspal Singh, and Manpreet Kaur. 2018. “Microstructure and Strength Development of Fly Ash-Based Geopolymer Mortar: Role of Nano-Metakaolin.” Construction and Building Materials, 190, 672-679. doi: 10.1016/j.conbuildmat.2018.09.157.

Kaya, Mehmet, Mucteba Uysal, Kemalettin Yilmaz, and Cengiz Duran Atis. 2018. “Behaviour of Geopolymer Mortars after Exposure to Elevated Temperatures.” Medziagotyra 24(4), 428-436. doi: 10.5755/

Kaya, Mehmet, Mücteba Uysal, Kemalettin Yilmaz, Okan Karahan, and C. Duran Atis. 2020. “Mechanical Properties of Class C and F Fly Ash Geopolymer Mortars.” Gradjevinar, 72(4), 297-309. doi: 10.14256/JCE.2421.2018.

Keke, Sun, Peng Xiaoqin, Wang Shuping, and Zeng Lu. 2019. “Design Method for the Mix Proportion of Geopolymer Concrete Based on the Paste Thickness of Coated Aggregate.” Journal of Cleaner Production, 232, 508-517. doi: 10.1016/j.jclepro.2019.05.254.

Ling, Yifeng, Kejin Wang, Wengui Li, Guyu Shi, and Ping Lu. 2019. “Effect of Slag on the Mechanical Properties and Bond Strength of Fly Ash-Based Engineered Geopolymer Composites.” Composites Part B: Engineering, 164, 106898. doi: 10.1016/j.compositesb.2019.01.092.

Ling, Yifeng, Peng Zhang, Juan Wang, and Yuanzhao Chen. 2019. “Effect of PVA Fiber on Mechanical Properties of Cementitious Composite with and without Nano-SiO2.” Construction and Building Materials, 229, 117068. doi: 10.1016/j.conbuildmat.2019.117068.

Montgomery, D. C. 2017. Design and Analysis of Experiments: Response Surface Method and Designs. UK: John Wiley and Sons Ltd.

Muraleedharan, Manjusha, and Yashida Nadir. 2021. “Factors Affecting the Mechanical Properties and Microstructure of Geopolymers from Red Mud and Granite Waste Powder: A Review.” Ceramics International 47(10, Part A), 13257–79. doi:

Neupane, Kamal. 2018. “High-Strength Geopolymer Concrete- Properties, Advantages and Challenges.” Advances in Materials, 7(2), 15-25. doi: 10.11648/

Niyilola Braima, Maryam, Ambrose Nworah Anozie, and Oludare Johnson Odejobi. 2016. Utilization of Response Surface Methodology (RSM) in the Optimization of Crude Oil Refinery Process, New Port-Harcourt Refinery, Nigeria. Vol. 3.

Okoye, F. N., J. Durgaprasad, and N. B. Singh. 2015. “Fly Ash/Kaolin Based Geopolymer Green Concretes and Their Mechanical Properties.” Data in Brief, 5, 739-734. doi: 10.1016/j.dib.2015.10.029.

Rahmiati, Tia, Khairun Azizi Azizli, Zakaria Man, Lukman Ismail, and Muhd Fadhil Nuruddin. 2014. “The Effect of KOH Concentration on Setting Time and Compressive Strength of Fly Ash-Based Geopolymer.” in Applied Mechanics and Materials, Vol. 625, 94-97.

Ravitheja, A., and N. L. N. Kiran Kumar. 2019. “A Study on the Effect of Nano Clay and GGBS on the Strength Properties of Fly Ash Based Geopolymers.” in Materials Today: Proceedings, 19, 273-276.

Rifaai, Yasser, Ammar Yahia, Ahmed Mostafa, Salima Aggoun, and El Hadj Kadri. 2019. “Rheology of Fly Ash-Based Geopolymer: Effect of NaOH Concentration.” Construction and Building Materials, 223, 583-594. doi: 10.1016/j.conbuildmat.2019.07.028.

Ritchie, Hannah, Esteban Ortiz-Ospina, Diana Beltekian, Edouard Mathieu, Joe Hassel, Bobbie Macdonald, Charlie Giattino, Cameron Appel, and Max Roser. 2021. “Our World in Data.” Retrieved (

Ryu, Gum Sung, Young Bok Lee, Kyung Taek Koh, and Young Soo Chung. 2013. “The Mechanical Properties of Fly Ash-Based Geopolymer Concrete with Alkaline Activators.” Construction and Building Materials, 47, 409-418. doi: 10.1016/j.conbuildmat.2013.05.069.

Şahin, Murat, Mahdi Mahyar, and Sinan T. Erdoğan. 2016. “Mutual Activation of Blast Furnace Slag and a High-Calcium Fly Ash Rich in Free Lime and Sulfates.” Construction and Building Materials, 126, 466-475. doi: 10.1016/j.conbuildmat.2016.09.064.

Sarıdemir, Mustafa, and Serhat Çelikten. 2020. “Investigation of Fire and Chemical Effects on the Properties of Alkali-Activated Lightweight Concretes Produced with Basaltic Pumice Aggregate.” Construction and Building Materials, 260, 119969. doi: 10.1016/j.conbuildmat.2020.119969.

Shi, Zhenguo, Caijun Shi, Shu Wan, and Zuhua Zhang. 2018. “Effects of Alkali Dosage and Silicate Modulus on Alkali-Silica Reaction in Alkali-Activated Slag Mortars.” Cement and Concrete Research, 111, 104-115. doi: 10.1016/j.cemconres.2018.06.005.

Sofi, M., J. S. J. van Deventer, P. A. Mendis, and G. C. Lukey. 2007. “Engineering Properties of Inorganic Polymer Concretes (IPCs).” Cement and Concrete Research, 37(2), 251-257. doi: 10.1016/j.cemconres.2006.10.008.

Tanyildizi, Harun, and Yavuz Yonar. 2016. “Mechanical Properties of Geopolymer Concrete Containing Polyvinyl Alcohol Fiber Exposed to High Temperature.” Construction and Building Materials, 126, 381-387. doi: 10.1016/j.conbuildmat.2016.09.001.

TS EN 1015-11. 2019. “Methods of Test for Mortar for Masonry-Part 11: Determination of Flexural and Compressive Strength of Hardened Mortar.”

TS EN 1015-3. 1999. “Methods of Test for Mortar for Masonry- Part 3: Determination of Consistence of Fresh Mortar (by Flow Table).”

TS EN 1015-11. 2019. “Methods of Test for Mortar for Masonry-Part 11: Determination of Flexural and Compressive Strength of Hardened Mortar.”

Wang, Yaguang, Xiaoming Liu, Wei Zhang, Zepeng Li, Yuliang Zhang, Yong Li, and Yongyu Ren. 2020. “Effects of Si/Al Ratio on the Efflorescence and Properties of Fly Ash Based Geopolymer.” Journal of Cleaner Production, 242, 118436. doi: 10.1016/j.jclepro.2019.118852.

Xu, Fang, Xin Deng, Chao Peng, Jing Zhu, and Jianping Chen. 2017. “Mix Design and Flexural Toughness of PVA Fiber Reinforced Fly Ash-Geopolymer Composites.” Construction and Building Materials, 150, 179-189. doi: 10.1016/j.conbuildmat.2017.05.172.

Xu, Shilang, Muhammad Akbar Malik, Zhang Qi, Bo Tao Huang, Qinghua Li, and Manas Sarkar. 2018. “Influence of the PVA Fibers and SiO2 NPs on the Structural Properties of Fly Ash Based Sustainable Geopolymer.” Construction and Building Materials, 164, 238-245. doi: 10.1016/j.conbuildmat.2017.12.227.

Zhang, Z. H., H. J. Zhu, C. H. Zhou, and H. Wang. 2016. “Geopolymer from Kaolin in China: an overview.” Applied Clay Science, 119, 31-41.




How to Cite

Kaya, M., & Köksal, F. (2021). Influences of high temperature on mechanical properties of fly ash based geopolymer mortars reinforced with PVA fiber. Revista De La Construcción. Journal of Construction, 20(2), 393–406.